城市污泥的灰分与水泥生料中粘土的成分类似,可被用作粘土的替代品煅烧生态水泥熟料,从而实现污泥的减量、无害、资源循环利用的可持续发展要求.本文用污泥灰替代粘土配置成掺量为0wt.％、3.58wt.％、7.16wt.％、10.73Wt.％和14.31Wt.％的生料并煅烧成熟料,再利用29Si固体高分辨核磁共振技术分析五种熟料的矿物成分,通过固体核磁分峰拟合技术得出五种熟料的贝利特和阿利特的含量比值,结果表明随着污泥灰掺量的增加,熟料中贝利特含量增加,阿利特含量降低,污泥中微量元素的引入使β-C2S更稳定,阻碍C2S向C3S的转化.
参考文献
| [1] | Tay JH;Show KY.Resource recovery of sludge as a building and construction material - A future trend in sludge management[J].Water Science and Technology,199711(11):259-266. |
| [2] | 方永浩.固体高分辨核磁共振在水泥化学研究中的应用[J].建筑材料学报,2003(01):54-60. |
| [3] | Soren L. Poulsen;Vanessa Kocaba;Gwenn Le Saout;Hans J. Jakobsen;Karen L Scrivener;Jorgen Skibsted.Improved quantification of alite and belite in anhydrous Portland cements by ~(29)Si MAS NMR: Effects of paramagnetic ions[J].Solid State Nuclear Magnetic Resonance,20091(1):32-44. |
| [4] | Chiou-Kuo Lin;Jong-Nan Chen;Cheng-Chong Lin.An NMR and XRD study of solidification/stabilization of chromium with Portland cement and β-C_2S[J].Journal of hazardous materials,19961/3(1/3):137-147. |
| [5] | 何永佳;胡曙光.29Si固体核磁共振技术在水泥化学研究中的应用[J].材料科学与工程学报,2007(1):147-153. |
| [6] | 肖建敏;范海宏.固体核磁共振技术在水泥及其水化产物研究中的应用[J].材料科学与工程学报,2016(1):166-172. |
| [7] | K.Johansson;C.Larsson.Kinetics of the hydration reactions in the cement paste with mechanochemically modified cement 29Si magic-angle-spinning NMR study[J].Cement and Concrete Research,199910(10):1575-1581. |
| [8] | 马先伟;贺孝一;傅蓉;陈胡星;沈锦林.BaO对高C3S熟料烧成的影响[J].材料科学与工程学报,2006(4):574-577. |
| [9] | 赵晓云;郭大刚;憨勇;徐可为.含锶磷酸钙骨水泥的制备及性能研究[J].无机材料学报,2005(5):1167-1173. |
| [10] | 宝志强;戴恒杰;蔡锐锋;陈胡星.污泥对水泥熟料烧成和强度的影响[J].材料科学与工程学报,2009(6):909-913. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%